Bonded NdFeB Magnet
Anisotropic Bonded NdFeB Magnet
Injection molded Ferrite and NdFeB Magnet
Injection Compound  Magnet
Polymer Coating
Introduction of Bonded NdFeB Magnet

    The Bonded NdFeB magnet is made by mixing binder and magnetic powder according to proportion, the production process is compression molding, magnetic features are as follows:

1)High precision: The required precision is obtained after one-shot molding, without further process    

2)Excellent magnetic properties: The Max. energy product is three times as large as  anisotropic ferrite magnet, the intrinsic coercive force is high. During the large-scale production, the magnetic properties are stable and the conformity is good.    

3)Good corrosion-resistance and nice surface, the product is coated with resin or Parylene, the anticorrosion is very good, and the surface is smooth, clean and nice-looking, without bubble, crack, strip-off and chip.

4)Various complex shapes and different modes of magnetization。

The products arewidely used in micro-motor, automobile industry, office automation, homeappliance, digital products, instrument, magnetic therapy and other fields.



Product Display
Product Application
Process flow Chart
Bonded NdFeB Magnet Properties Table


牌号/Grade
MSM-2
MSM-4
MSM-6
MSM-8
MSM-8L
MSM-8SR
MSM-8H
剩余磁感应强度Br(mT
Residual Induction(KGs)
300-400
(3.0-4.0)
400-500
(4.0-5.0)
500-600
(5.0-6.0)
600-680
(6.0-6.8)
600-680
(6.0-6.8)
600-650
(6.0-6.5)
600-650
(6.0-6.5)
矫顽力Hcb(KA/m)
Coercive Force(Koe
160-240
(2.0-3.0)
240-320
(3.0-4.0)
320-400
(4.0-5.0)
360-440
(4.5-5.5)
400-480
(5.0-6.0)
400-480
(5.0-6.0)
400-480
(5.0-6.0)
內禀矫顽力Hcj(KA/m)
Intrinsic Coercive Force(Koe
480-640
(6.0-8.0)
560-720
(7.0-9.0)
560-720
(7.0-9.0)
640-800
(8.0-10.0)
640-800
(8.0-10.0)
800-1120
(10.0-14.0)
1040-1360
(13.0-17.0)
最大磁能积(BH)max(KJ/m³
Max.Energy Product(MGOe
16-24
(2.0-3.0)
32-44
(4.0-5.5)
48-60
(6.0-7.5)
60-72
(7.5-9.0)
64-72
(8.0-9.0)
60-68
(7.5-8.5)
60-68
(7.5-8.5)
可逆透磁率 μr/Recoil
Permeability (μH/M)
1.2
1.2
1.2
1.2
1.2
1.2
1.2
平均可逆温度系数(%/℃)
Temperature Coefficient
-0.11
-0.11
-0.11
-0.11
-0.11
-0.11
-0.11
居里温度Tc(℃)
Curie Temperature
350
350
350
350
300
300
300
最大工作温度(℃)
Max.Operating  Temperature
160
160
160
160
160
180
160
饱和磁化场Saturation(KA/m)
Magnetizing Force
>1600
>20
>1600
>20
>1600
>20
>1600
>20
>1600
>20
>2000
>25
>2400
>30
密度ρ (g/m³
Density
4.5-5.0
5.2-5.7
5.5-6.0
5.8-6.1
5.8-6.1
5.8-6.1
5.8-6.1
硬度HRB
Hardness
40-45
40-45
40-45
35-38
35-38
35-38
35-38


牌号/Grade
MSM-10
MSM-10H
MSM-12
MSM-12L
MSM-12D
MSM-13L
-
剩余磁感应强度Br(mT
Residual Induction(KGs)
680-730
(6.8-7.3)
700-750
(7.0-7.5)
720-770
(7.2-7.7)
760-810
(7.6-8.1)
720-770
(7.2-7.7)
780-830
(7.8-8.3)
-
矫顽力Hcb(KA/m)
Coercive Force(Koe
400-480
(5.0-6.0)
400-480
(5.0-6.0)
440-520
(5.5-6.5)
400-480
(5.0-6.0)
440-520
(5.5-6.5)
400-480
(5.0-6.0)
-
內禀矫顽力Hcj(KA/m)
Intrinsic Coercive Force(Koe
640-800
(8.0-10.0)
640-800
(8.0-10.0)
720-880
(9.0-11.0)
480-640
(6.0-8.0)
720-880
(9.0-11.0)
480-640
(6.0-8.0)
-
最大磁能积(BH)max(KJ/m³
Max.Energy Product(MGOe
76-84
(9.5-10.5)
80-88
(10.0-11.0)
88-96
(11.0-12.0)
88-96
(11.0-12.0)
88-96
(11.0-12.0)
88-104
(11.0-13.0)
-
可逆透磁率 μr/Recoil
Permeability (μH/M)
1.2
1.2
1.2
1.2
1.2
1.2
-
平均可逆温度系数(%/℃)
Temperature Coefficient
-0.10
-0.10
-0.10
-0.11
-0.08
-0.11
-
居里温度Tc(℃)
Curie Temperature
350
350
350
320
400
320
-
最大工作温度(℃)
Max.Operating  Temperature
160
160
160
150
170
150
-
饱和磁化场Saturation(KA/m)
Magnetizing Force
>1600
>20
>1600
>20
>1600
>20
>1600
>20
>2000
>25
>1600
>20
-
密度ρ (g/m³
Density
5.8-6.1
6.0-6.3
6.0-6.3
6.0-6.3
6.0-6.3
6.1-6.4
-
硬度HRB
Hardness
35-38
35-38
35-38
35-38
35-38
35-38
-




Magnetic Poles Display
Axial multi-pole magnetization
Outer diameter multi-pole magnetization
Inner diameter multi-pole magnetization
Surface multi-pole magnetization
Diametrical magnetization
Radial multi-pole magnetization
Skewed multi-pole magnetization
Skewed multi-pole magnetization
Introduction of Anisotropic Bonded NdFeB Magnet

     Anisotropic Bonded NdFeB magnet with high magnetic properties, compression molding and curing by low temperature avoid deformation. With high precision dimension and good consistency, multi-pole magnetization can be achieved easily, low torque ,large output and high temperature resistance can be realized by special magnetic design. The products have good toughness, not easy to be broken, they are widely used in all kinds of micro-motors to reduce the weight, noise and volume of the motors, improving the efficiency and saving energy.


Product Display
Product Application
Process flow chart
Anisotropic Bonded NdFeB Magnet Properties table


   

 Product

   

Grade

剩余磁感应强度
(Br)/T
矫顽力
Hcb/Koe
矫顽力
Hcj/Koe
最大磁能积   (BH)max/MGOe
NdFeB系列
MSM-YMN-10-10
6.77.4
5.3~5.6
9.0~11.0
9~11
MSM-YMN-13-12
7.4~8.6
5.6~6.1
11.0~13.0
11~14
MSM-YMN-15-12
8.6~8.8
6.1~6.6
11.0~13.0
14~16
MSM-YMN-17-13
8.8~9.4
6.6~6.8
12.0~14.0
16~18
MSM-YMN-19-13
9.4~9.8
6.8~7.3
12.0~14.0
18~20



Anisotropic Bonded NdFeB Magnet V.S other Magnets
Introduction

     Injection molded ferrite and injection molded  NdFeb magnet ( isotropy and anisotropy)have excellent toughness, according to customer’s requirements ,magnet can be combined with plastic or metal parts perfectly through injection one-step molding, various complex shapes and magnetizing methods are available, the surface is smooth, clean, flawless and with high shock resistance. The products are with high precision dimension and good consistence, whole assembley supply to help customers realize cost saving.

Product Display
Injection ferrite
PPS+NdFeB Magnet
Injection ferrite
Product Application
Injection Molded Magnet Process Flow Chart

Magnetic Methods


Product Magnetic Properties And Physical Propertie
Introduction of Injection Compound magnet

According to customer’s requirements, magnet can be combined with plastic or metal parts perfectly through injection one-step molding, various complex shapes and magnetizing methods are available , with high precision dimension and good consistency, the magnetic property is stable. Imported raw material, guarantee the safety; Whole assembly supply, without secondary processing, to help customers realize cost saving.

Product Application
Product Display
Introduction of Polymer Coating

网易彩票     Polymer coating is a contraction of "high density polymer resin coating". Similar to Japanese traditional URUSHI coating, the product is coated and dried many times, with super multi layer and high density without a pin-hole. This structure gives the advantages in electric insulation, rust resistance and adhesion.  Polymer coating is halogen-free and environmental friendly, also with many colors.


Product Display
Product Application
Polymer Coating Properties After Curing



性能/Performance
描述/Description
  •   耐热

    Heat resistance
  • 250℃可连续工作,瞬间可以在300℃
  • Can work continuously at 250 ℃ , instantaneously at 300 ℃.
绝缘
      Insulation
最大可实现1.5KV/20µm(根据材料不同)
Max 1.5KV/20µm (varies from different material).
切割
Cutting
涂装后可以切开产品而涂层不会剥落,因此可以实现微小铁芯绕线的自动化.
  • Coating is not peeled off when cutting the products, thus automatic tiny core    windingcan be realized.
防锈
Anti-rust
SST试验500小时以上
  • SST test more than 500 hours.
粘接力
Adhesion
是镀镍的5倍以上,适用于稀土永磁
  • 3 to 5 times higher than electroplating, good for rare earth magnet.
伸缩性
Flexibility
防止微小铁芯的碎片飞散对周边部件产生影响。喷涂后金属片可以弯着而涂层不受影响

Coating is not affected when bending the coated metal sheets, no coating chipsfall  off  

均匀涂层
Uniform coated
产品的边角处皆可均匀涂覆,适合于EMC铁芯的涂装

The edges and corners of the product can be evenly coated. Suitable for EMC core   coating.

公差小
Tiny tolerances
批量生产中的尺寸公差、偏差可控制到很小
  • Tiny tolerancesduring the batch production.
颜色
Color
可以调节成各种颜色,适用于利用颜色区分不同的电子产品,以及使饰品的具有独家特色

Richcolors, suitable for the use of color to distinguish different electronicproducts,  and make jewelry with exclusive features.

抗化学药剂

Anti-chemical agent

可用于马达的碱性油中
  • Can be used in basic oil of motor.

无过敏性

No allergies

应用在医疗器械以及各种饰品(例如医疗器械胃镜的部件)
  • Used in medical devices and various accessories (such as components of medical instruments for gastroscopy).
RoHS,无卤素
halogen free
对应RoHS,以及卤素
halogen free, conform to RoHS standards.

L值(电感)

L value - inductance

喷涂过程中对产品的负担小,对于L值无大的影响
  • In process of spraying, burden on the product is small and no influence on the  Lvalue.
强度
Strength
铅笔硬度测试在5H以上
  • Pencil hardness test above 5 hours.



Polymer Coating V.S Other Coatings


CONTACT

Mobile Phone:13418399067 Tel:+86-769-23366926   81662156 Email:sales@magsuper.cn
About

Development history Corporate culture
Service and Support Company environment Corporate honor

Product introduction

Bonded Nd-Fe-B homosexual
magnet
Anisotropic NdFeB magnet
Plastic Ferrite Magnets & Plastic
NdFeB Magnets(Isotropic and
Anisotropic)
Injection molded composite
magnetic parts
Polymer Coating
News

Enterprise dynamics Industry news
Contact

Contact nformation
Online Message
Magsuper (Dong Guan) Corp.
Address:Shang Gaotian Village, LianPing District, Da Lingshan Town, Dong Guan City, Guang Dong Province, China
在线客服
 
 
 
 
 Work Time
Mon to Fri :8:00-17:30
Sat to Sun :9:00-17:00
 Contact Details
客服热线:0769-81662156
客服热线:0769-85780817
邮箱:sales@magsuper.cn
欢乐彩票-官网 易购彩票_易购彩票|平台 光大彩票-官网 欢乐彩票-官网 易购彩票_ 人人中彩票帝皇彩票